UNI-1056
Cadmium Free 56% Silver Solder
|
 |
- Low
melting point
-
Very well suited to brazing leaded brass
-
Brazing of screw machine parts, pump cylinders and
gears
-
Ideal for brazing the following base metals: Nickel
and Nickel Alloys, Stainless Steel
|
Joining stainless materials commonly used in the food and dairy
industry. Excellent for assembly and repair of laboratory apparatus
including tubing instruments and control devices. Ideally suited
for general maintenance and repair work. |
| Technical
Data |
| Nominal
Composition |
|
| 56%
Silver, 22% Copper, 17% Zinc, 5% Tin |
|
| Tensile
Strength |
65,000
PSI (51Kg/MM2)
|
| Solidus |
1145°F
(618°C)
|
| Liquidus |
1205°F
(652°C)
|
| Color
as brazed |
White |
| Corrosion
resistance |
Good |
| Electrical
conductivity |
Good |
| Diameter
(in) |
1/16"
3/32" |
| (cm) |
1.6mm
2.5mm |
| Specifications |
|
| AWS |
A5.8
Class BAg-7
|
| ASME |
SAF5.8
Class BAg/7
|
| FED. |
QQB654A
Grade BAg-5(I)
|
|
| Procedure |
| Thoroughly
clean and degrease the joint area. When using bare rod, paint
UNI-1000 flux on the rod and joint area. Heat broadly with a
carburizing flame until flux has liquified. Apply UNI-1056 until
alloy flows through the joints. Cool slowly and remove flux
residues with warm water. |